1. Common Fiber: Manufactured from hard clay clinker as the raw material, produced by melting and blowing, and spun using a resistance furnace.
2. High-Purity Fiber: Manufactured from high-purity alumina and silica as raw materials, produced by melting and blowing, and spun using a resistance furnace.
3. Cerachem Fiber: Manufactured from alumina, silica, and zirconia as raw materials, produced by melting and blowing, and spun using a resistance furnace.
4. Cerachrome Fiber: Manufactured from alumina, silica, and chromia as raw materials, produced by melting and blowing, and spun using a resistance furnace.
5. Spun Fiber: Contains lubricant, features low shot content and high fiber content, and is spun without further processing to form long fibers. It is used as gap-filling material for the wall linings of high-temperature kiln heating equipment and as a raw material for yarn production.
6. Blown Fiber: Contains no lubricant and requires no further processing, features low shot content, and is used as gap-filling material for high-temperature kilns, as well as a raw material for vacuum-formed products, fiber spraying, and fiber paper.
1. Excellent thermal stability, resist devitrification at high temperature.
2. Low heat strong capacity, Low thermal conductivity
3. Contain no binders or corrosive agents
4. Resilient up to high temperatures
5. Excellent sound absorber
1. Raw material for the manufacturing of finished products such as boards, paper, shapes, yarns etc.
2. Packing expansion joints and material for temporary repair of insulation
3. Raw material for Fiber spraying, castable and daub material
4. Loose insulating fill for complex spaces and areas where access is difficult
Type | CT 1000 | CT 1260 | CT 1350 | CT 1430 | CT 1500 | CT 1600 | |
|---|---|---|---|---|---|---|---|
ClassificationTemperture℃ | 1000 | 1260 | 1350 | 1430 | 1500 | 1600 | |
Color | White | Pure White | Pure White | Pure White | Blue/Green | White | |
Chemical Composition | Al₂O₃ | ≥38 | ≥43 | ≥37 | ≥37 | ≥37 | ≥72 |
Al₂O₃+SiO₂ | ≥95 | ≥97 | ≥92 | ≥83 | ≥93 | ≥99 | |
Al₂O₃+SiO₂ +ZrO₂(Cr₂O₃) | -- | -- | 99 | 99 | 99 | -- | |
ZrO₂ | -- | -- | 5-7 | 15-17 | -- | -- | |
Cr₂O₃ | -- | -- | -- | -- | 2.0-3.8 | -- | |